RESUMEN
This investigation considered the usability of ceramic waste powder (CWP) in altered quantities in reinforced concrete beams (RCBs). In this way, it was aimed to reduce the environmental impacts of concrete by using CWP as a raw material in RCBs. 12 small-scale shear RCBs with the dimensions of 100 × 150 × 1000 mm were tested in this study. The variations of stirrups spacing and CWP ratio were examined in these specimens. The percentages of CWP by weight utilized in RCBs were 10%, 20%, and 30%, and stirrups spacings were adopted as 270 mm, 200 mm, and 160 mm. At the end of the study, it was determined that more than 10% CWP additive negatively affected the RCBs' compressive strength. The load-carrying capacity reduced between 30.3% and 59.4% when CWP increased from 0% to 30% as compared to RCB with stirrups spacing of 270 mm without CWP. However, compared to RCB with stirrups spacings of 200 mm and 160 mm without CWP, there were decreases in the load-carrying capacity as 21.4%-54.3% and 18.6%-54.6%, respectively. While the CWP ratio increased, the specimens with 160 mm, 200 mm, and 270 mm stirrups spacings obtained a lower maximum load value. However, with the increase of the CWP ratio in the specimens with 160 mm stirrups spacing, RCBs reached the maximum load-carrying capacity at an earlier displacement value. When stirrups spacing was selected as 270 mm, it was observed that the maximum load-carrying capacity of RCBs reached at a similar displacement value as the CWP ratio increased. Besides, it was resulted that the bending stiffness of RCBs reduced as the quantity of CWP enhanced. The bending stiffness decreased by 29.1% to 66.4% in the specimens with 270 mm stirrups spacing, 36.3% to 20.2% with 200 mm stirrups spacing, and 10.3% to 36.9% with 160 mm stirrups spacing. As an implication of the experiments, the use of CWP up to 10% in RCBs was realized as an economical and environmental approach and is suggested. There is some evidence to report that making use of CWP may be considered to be ecologically benign. This is due to the fact that reusing CWP may significantly reduce CO2 emissions, save energy, and reduce total power consumption. Furthermore, the experimental results were compared to the analytical calculations.
RESUMEN
The intent of this study is to explore the physical properties and long-term performance of concrete made with metakaolin (MK) as a binder, using microsilica (MS) and nanosilica (NS) as substitutes for a portion of the ordinary Portland cement (OPC) content. The dosage of MS was varied from 5% to 15% for OPC-MK-MS blends, and the dosage of NS was varied from 0.5% to 1.5% for OPC-MK-NS blends. Incorporation of these pozzolans accelerated the hardening process and reduced the flowability, consistency, and setting time of the cement paste. In addition, it produced a denser matrix, improving the strength of the concrete matrix, as confirmed by scanning electron microscopy and X-ray diffraction analysis. The use of MS enhanced the strength by 10.37%, and the utilization of NS increased the strength by 11.48% at 28 days. It also reduced the penetrability of the matrix with a maximum reduction in the water absorption (35.82%) and improved the resistance to the sulfate attack for specimens containing 1% NS in the presence of 10% MK. Based on these results, NS in the presence of MK can be used to obtain cementitious structures with the enhanced strength and durability.